In Situ TEM Observation of Toughening Mechanisms in Ultra-fine Grained Columnar Aluminum Thin Films
Disassociation of a Bend Contour due to Dislocation Activity
Fracture Parallel to Tensile Axis
Crack Bypass Mechanism of a Large Grain with possible Deformation Twin